Extremely high viscosity grease with solid lubricants

Extremely high viscosity grease with solid lubricants

Photo LGEV 2

SKF LGEV 2 is a mineral oil based grease, using a lithium-calcium soap. Its high content of molybdenum disulphide and graphite, in conjunction with an extremely high viscosity oil, provide outstanding protection under the harshest conditions involving high loads, slow rotations and severe vibrations.

Extremely suitable for lubricating large sized spherical roller bearings subject to high loads and slow rotations, a situation where microslip is likely to occur

Extremely mechanically stable providing good water resistance and corrosion protection

Typical applications:

Trunnion bearings on rotating drums

Support and thrust rollers on rotary kilns and dryers

Bucket wheel excavators

Slewing ring bearings

High pressure roller mills

Crushers

Available pack sizes
Packsize Designation
35 g tube LGEV 2/0.035
420 ml cartridge LGEV 2/0.4
5 kg can LGEV 2/5
18 kg pail LGEV 2/18
50 kg drum LGEV 2/50
180 kg drum LGEV 2/180
Electro-mechanical lubricant dispensers  
TLMR 101 series 380 ml refill (incl. battery) LGEV2/MR 380B
TLMR 201 series 380 ml refill LGEV 2/MR380
Technical data
Designation LGEV 2/(pack size)
DIN 51825 code KPF2K-10
NLGI consistency class 2
Thickener Lithium/calcium
Colour Black
Base oil type Mineral
Operating temperature range –10 to +120 °C

(15 to 250 °F)
Dropping point DIN ISO 2176 >180 °C (>355 °F)
Base oil viscosity  
40 °C, mm²/s

100 °C, mm²/s
1 020

58
Penetration DIN ISO 2137  
60 strokes, 10–1 mm

100 000 strokes, 10–1 mm
265–295

325 max.
Mechanical stability  
Roll stability, 72 hrs at 100 °C, 10–1 mm

V2F test
+50 max.

‘M’
Corrosion protection  
Emcor:
– standard ISO 11007

– water washout test

– salt water test  (100% seawater)
0–0

0–0*

0–0*
Water resistance  
DIN 51 807/1, 3 hrs at 90 °C 1 max.
Oil separation  
DIN 51 817, 7 days at 40 °C, static, % 1–5
Copper corrosion  
DIN 51 811
1 max 100 °C (210 °F)
EP performance  
Wear scar DIN 51350/5, 1 400 N, mm

4–ball test, welding load DIN 51350/4, N
1,2 max.

3 000 min.
* Typical value